Table 3 Characteristics and mechanical properties of the saturant
From: Influence of fibre reinforced polymers in the rehabilitation of damaged masonry wallettes
Properties | |||
|---|---|---|---|
Compressive | Tensile | Flexural | |
Yield strength | 86.2 MPa | 54.0 MPa | 138.0 MPa |
Strain at yield | 5.0% | 2.5% | 3.8% |
Elastic modulus | 2620 MPa | 3034 MPa | 3724 MPa |
Ultimate strength | 86.2 MPa | 55.2 MPa | 138.0 MPa |
Rupture strain | 5.0% | 3.5% | 5% |
Poisson’s ratio | _ | 0.40 | _ |
Pot life | 45 min at 25°C | ||
Cure | Fully cured at 20°C - 7 days | ||