Table 1 Materials, manufacturer, composition and application

From: In vitro evaluation of the shear bond strength between fiber posts and methacrylate or silorane based composite resins

Material/manufacturer Composition Application
Filtek™ Z250, A2 Shade, 3 M/ESPE 75–85 % silanized ceramic; 1-10 % BISEMA6; 1–10 % UDMA; 1–10 % BIS-GMA; <5 % TEGDMA; <5 % aluminum oxide; <0.5 % benzotriazole; <0.2 % EDMAB 2.5 mm maximum increment, photo-activated for 80 s
Filtek™ P90, A2 Shade, 3 M/ESPE 5–15 % 3,4-epoxi-ciclohexil-ethyl-cyclopolimethyl-siloxane; 5–15 % bis-3,4-epoxi-ciclohexil-ethyl-fenil-methyl-silane; 50–70 % silanized quartz; 10–20 % Yttrium fluoride; camphorquinone 2.5 mm maximum increment, photo-activated for 80 s
Filtek™ Bulk Fill Restorative, A2 Shade, 3 M/ESPE 60–70 % silanized ceramic; 10–20 % aromatic di methacrylate urethane; 1–10 % Ytterbium fluoride; 1-10 % UDMA; 1–10 % silanized silica; <5 % DDDMA; <5 % water; <5 % silanized zirconium; <1 % modified methacrylate monomer; <0.5 % EDMAB; <0.5 % benzotriazole 2.5 mm maximum increment, photo-activated for 80 s
Scotchbond™ Universal, 3 M/ESPE 15–25 % BIS-GMA; 15-25 % HEMA; 5-15 % deca methylene di methacrylate; 10–15 % ethanol; 10–15 % water; 5–15 % silanized silica; 1–10 % propenoic acid, 2-methyl, decanediole and phosphoric anidryde byproducts; 1-5 % itaconic and acrylic co-polymer acids; <2 % dimethyl amine benzoate; <2 % camphorquinone; <2 % dimethyl amine ethyl methacrylate; <2 % methyl ethyl ketone Application of a thin layer for 15 s, Air drying for 5 s, Light-curing for 20 s
Filtek™ P90 SA, 3 M/ESPE Primer: 15–25 % HEMA; 15–25 % BIS-GMA; 10–15 % water; 10–15 % ethanol; 5–15 % phosphoric acid methacryl-oxi-hexil-esters; 8–12 % silanized silica; 5–10 % 1,6-hexanediol di methacrylate; <5 % itaconic and acrylic acid co-polymer; <5 % (dimethyl amine) ethyl methacrylate; <3 % DL- camphorquinone; <3 % phosphine oxide; Bond: 70–80 % replaced di methacrylate; 5–10 % silanized silica; 5–10 % TEGDMA; <5 % phosphoric acid methacryl-oxi-hexil-esters; <3 % DL-camphorquinone; 1,6 hexanediol di methacrylate Homogenous bond application, Light-curing for 20 s
Exacto Translúcido #03, Angelus® 80 % glass fiber, 20 % epoxy resin Cleansing with ethanol 70 % for 15 s
Silano Angelus® X-R–Si (OR) 3n, X: organic-functional group bonds to composite resin, R: methylene group, OR: hydrolysable group bonds with porcelains, composite resins and glass fiber posts, Si: Silicium. n: 0–3 Thin layer application 60 s waiting time Smooth air drying for 5 s
  1. BISEMA6 bisphenol a polyethylene glycol diether dimethacrylate; UDMA diurethane dimethacrylate; BISGMA bisphenol a diglycidyl ether dimethacrylate; TEGDMA triethylene glycol dimethacrylate: EDMAB ethyl 4-dimethyl aminobenzoate; HEMA 2-hydroxyethyl methacrylate
\