From: Comparative study of adhesive joint designs for composite trusses based on numerical models
Property | Araldite 2015 |
---|---|
Young’s modulus (GPa) | 1.85 ± 0.21 |
Poisson’s ratio | 0.33 |
Tensile yield strength (MPa) | 12.63 ± 0.61 |
Tensile yield strain (%) | 0.06 ± 0.05 |
Tensile failure stress (MPa) | 21.63 ± 1.61 |
Tensile failure strain (%) | 4.77 ± 0.15 |
Shear modulus (GPa) | 0.56 ± 0.21 |
Shear yield stress (MPa) | 14.6 ± 1.3 |
Shear failure stress (MPa) | 17.9 ± 1.8 |
Shear failure strain (%) | 43.9 ± 3.4 |
Density (g/cm3) | 1.4 |