From: Influence of technological procedures on mechanical properties of bonded joint
Order combination | Failure mode | Order combination | Failure mode | Order combination | Failure mode |
---|---|---|---|---|---|
0th | CF (100%) | 11th | A/C − F (100%) | 22nd | CF (16%) A/C − F (84%) |
1st | CF (100%) | 12th | AF (50%) A/C − F (50%) | 23rd | A/C − F (100%) |
2nd | CF (100%) | 13th | A/C − F (100%) | 24th | CF (16%) A/C − F (84%) |
3rd | CF (100%) | 14th | A/C − F (100%) | 25th | A/C − F (34%) AF (66%) |
4th | CF (100%) | 15th | AF (50%) A/C − F (50%) | 26th | A/C − F (34%) AF (66%) |
5th | A/C − F (16%) CF (84%) | 16th | CF (100%) | 27th | AF (100%) |
6th | CF (100%) | 17th | AF (34%) A/C − F (66%) | 28th | AF (100%) |
7th | CF (100%) | 18th | AF (34%) A/C − F (66%) | 29th | A/C − F (100%) |
8th | CF (100%) | 19th | AF (50%) A/C − F (50%) | 30th | A/C − F (100%) |
9th | CF (100%) | 20th | CF (16%) A/C − F (84%) | 31st | A/C − F (100%) |
10th | CF (100%) | 21st | A/C − F (100%) |